Bar Magnets Usage
How do you remove iron powder which has attached to the bar magnet?
It can be easily removed by patting over it using sticky tape.
Maintenance and replacement time
The stainless case is 0.5mm thick.
It may become thinner due to the hardness of the magnetic substance and contact friction.
Although the embedded magnets are permanent magnets, they have been embedded by applying resistance load.
Therefore, even if the magnets are used within the specification heat resistance temperature, they may demagnetize over time due to the repeated stress of fluctuating between hot and cold temperatures.
There is no definite timing for replacement, however we recommend regularly conducting surface magnetic flux density and appearance tests.
Bar Magnets Usage
What is the recommended distance between each bar?
When laying out the bars, the distance between each bar is important.
Please adjust the processing speed suitable for your productivity according to the distance between the bars.
The distance is determined by what kind of magnetic substance you would like to process and at what speed.
How often is maintenance and replacement required?
The stainless case is 0.5mm thick.
It may become thinner due to the hardness of the magnetic substance and contact friction.
Although the embedded magnets are permanent magnets, they have been embedded by applying resistance load.
Therefore, even if the magnets are used within the specification heat resistance temperature, they may demagnetize over time due to the repeated stress of fluctuating between hot and cold temperatures.
There is no definite timing for replacement, however we recommend regularly conducting surface magnetic flux density and appearance tests.
Narrow spaces
This will be a fine filter and the processing speed for separating magnetic substances will be slow.
Wide spaces
This will be a rougher filter and the processing speed for separating magnetic substances will be faster.
*In this case, the roughness of the filter and processing speed can be improved by making more than 2 layers of magnetic filters.
*If there are multiple layers with narrow spaces in between the bars, although the processing speed will be slower, the attraction capacity will increase.
Ring Tube Axially Magnetized Neodymium Permanent Rare Earth Magnet
Unipole Radially Magnetized Tube Magnet NdFeB N38SH
SS304 / SS316 Ferrite Ceramic Magnetic Tube Filter
Rare Earth Neodymium Magnetic Filter Tubes
Customized Multi-stage Magnetization Ferrite Anisotropic Tube Magnet
Multi-polar Sintered NdFeB Ring Tube Magnets N55